| Wrought aluminum alloy 1350 | ||||
| Chemical composition: Si=0.1%, Fe =0.40% , Al=99.5% min | ||||
| Property | Value in metric unit | Value in US unit | ||
| Density | 2.705 *10³ | kg/m³ | 169 | lb/ft³ |
|---|---|---|---|---|
| Modulus of elasticity | 69 | GPa | 10000 | ksi |
| Thermal expansion (20 ºC) | 23.8*10-6 | ºCˉ¹ | 13.2*10-6 | in/(in* ºF) |
| Specific heat capacity | 900 | J/(kg*K) | 0.215 | BTU/(lb*ºF) |
| Thermal conductivity | 234 | W/(m*K) | 1625 | BTU*in/(hr*ft²*ºF) |
| Electric resistivity | 2.83*10-8 | Ohm*m | 2.83*10-6 | Ohm*cm |
| Tensile strength (annealed) | 83 | MPa | 12000 | psi |
| Yield strength (annealed) | 28 | MPa | 4000 | psi |
| Elongation (annealed) | 23 | % | 23 | % |
| Shear strength (annealed) | 55 | MPa | 8000 | psi |
| Hardness (annealed) | 23 | HB | 23 | HB |
| Tensile strength (H16) | 124 | MPa | 18000 | psi |
| Yield strength (H16) | 110 | MPa | 16000 | psi |
| Elongation (H16) | 3 | % | 3 | % |
| Shear strength (H16) | 76 | MPa | 11000 | psi |
| Hardness (H16) | 34 | HB | 34 | HB |
| Annealing temperature | 343 | ºC | 650 | ºF |